Thermotropic liquid crystalline polymer with improved low shear viscosity

ABSTRACT

A thermotropic liquid crystalline polymer melt polymerized in the presence of a viscosity modifier that can help increase the “low shear” viscosity of the resulting composition is provided. The increased “low shear” viscosity can minimize drooling of the polymer composition during processing and also allow it to possess a greater melt strength, which facilitates its ability to be processed in a wide variety of applications without losing its physical integrity. Despite having a relatively high “low shear” viscosity, the present inventors have discovered that the viscosity modifier does not substantially increase the “high shear” melt viscosity of the polymer composition. In this regard, the ratio of the “low shear” viscosity to the melt viscosity is generally very high, such as within a range of from about 50 to about 1000.

RELATED APPLICATIONS

The present application claims priority to U.S. provisional application Ser. Nos. 61/528,401, filed on Aug. 29, 2011, and 61/664,881, filed on Jun. 27, 2012, which are incorporated herein in their entirety by reference thereto.

BACKGROUND OF THE INVENTION

Thermotropic liquid crystalline polymers are classified as “rigid rod” polymers as their molecular structure is typically composed of aromatic units linked by functional groups such as esters and/or amides. The rigid, rod-like structure allows the polymers to exhibit liquid crystalline behavior in their molten state (thermotropic nematic state). Due to the presence of this nematic state in the melt, these materials also exhibit unique rheological properties. One such property is a “shear thinning behavior” characterized by a decrease in complex viscosity with increasing shear rates. This high shear thinning behavior is particularly attractive in the fabrication of parts with intricate geometries (e.g., electrical connectors) because the polymers can flow well under heat and shear to uniformly fill complex parts at fast rates without excessive flashing or other detrimental processing issues. Despite these benefits, conventional liquid crystalline polymers sometimes exhibit a reduced “low shear” shear viscosity that can lead to “drooling” during processing, thereby leading to problems in uniformly filling the part. Furthermore, such polymers may also have a lower melt strength during melt processing, making it difficult for the resulting material to maintain its physical integrity. The lack of adequate melt strength and physical integrity becomes particularly problematic in non-molding applications, such as when the polymer is thermoformed into a sheet or film. Attempts have been made to increase the “low shear” viscosity by increasing the molecular weight of the polymer. However, this also increases the “high shear” viscosity, which can compromise the flow of the material.

As such, a need exists for a liquid crystalline polymer composition that exhibits excellent rheological properties under both low and high shear conditions, as well as a method of forming such polymers.

SUMMARY OF THE INVENTION

in accordance with one embodiment of the present invention, a thermotropic liquid crystalline polymer composition is disclosed that comprises a liquid crystalline polymer that is melt polymerized in the presence of an aromatic amide oligomer. The polymer composition exhibits a certain complex viscosity determined by a parallel plate rheometer at an angular frequency of 0.15 radians per second, temperature of 350° C., and constant strain amplitude of 1%, and a certain melt viscosity determined by a capillary rheometer at a shear rate of 1000 seconds⁻¹ and temperature of 350° C. The ratio of the complex viscosity to the melt viscosity is from about 50 to about 1000.

In accordance with another embodiment of the present invention, a method for forming a liquid crystalline polymer is disclosed. The method comprises melt polymerizing two or more monomers in the presence of an aromatic amide oligomer having a molecular weight of from about 450 to about 5,000 grams per mole. The monomers are precursors for the liquid crystalline polymer, and the aromatic amide oligomer has the following general formula (I):

wherein,

rings A and B are independently a 6-membered aromatic ring wherein 1 to 3 ring carbon atoms are optionally replaced by nitrogen or oxygen, wherein each nitrogen is optionally oxidized, and wherein rings A and B may be optionally fused or linked to a 5- or 6-membered aryl, heteroaryl, cycloalkyl, or heterocyclyl;

R₅ is halo, haloalkyl, alkyl, alkenyl, aryl, heteroaryl, cycloalkyl, or heterocyclyl;

m is from 0 to 4;

X₁ and X₂ are independently C(O)HN or NHC(O); and

R₁ and R₂ are independently selected from aryl, heteroaryl, cycloalkyl, and heterocyclyl.

Other features and aspects of the present invention are set forth in greater detail below.

BRIEF DESCRIPTION OF THE FIGURES

A full and enabling disclosure of the present invention, including the best mode thereof to one skilled in the art, is set forth more particularly in the remainder of the specification, including reference to the accompanying figures, in which:

FIG. 1 is the Proton NMR characterization for N1, N3,N5-tris(4-benzamidophenyl)benzene-1,3,5-tricarboxamide (Compound B).

FIG. 2 is the Proton NMR characterization for N4-phenyl-N1-[3-[[4-(phenylcarbamoyl)benzoyl]amino]phenyl]terephthalamide (Compound D2).

FIG. 3 is the Proton NMR characterization for N3-phenyl-N1-[3-[[3-(phenylcarbamoyl)benzoyl]amino]phenyl]benzene-1,3-dicarboxamide (Compound E2).

FIG. 4 is a graph showing complex viscosity (Pa*s) versus frequency (rad/s) for the samples of Examples 1, 4, and 5.

DETAILED DESCRIPTION OF REPRESENTATIVE EMBODIMENTS Definitions

It is to be understood that the terminology used herein is for the purpose of describing particular embodiments only and is not intended to limit the scope of the present invention.

“Alkyl” refers to monovalent saturated aliphatic hydrocarbyl groups having from 1 to 10 carbon atoms and, in some embodiments, from 1 to 6 carbon atoms. “C_(x-y)alkyl” refers to alkyl groups having from x to y carbon atoms. This term includes, by way of example, linear and branched hydrocarbyl groups such as methyl (CH₃), ethyl (CH₃CH₂), n-propyl (CH₃CH₂CH₂), isopropyl ((CH₃)₂CH), n-butyl (CH₃CH₂CH₂CH₂), isobutyl ((CH₃)₂CHCH₂), sec-butyl ((CH₃)(CH₃CH₂)CH), t-butyl ((CH₃)₃C), n-pentyl (CH₃CH₂CH₂CH₂CH₂), and neopentyl ((CH₃)₃CCH₂).

“Alkenyl” refers to a linear or branched hydrocarbyl group having from 2 to 10 carbon atoms and in some embodiments from 2 to 6 carbon atoms or 2 to 4 carbon atoms and having at least 1 site of vinyl unsaturation (>C═C<). For example, (C_(x)-C_(y))alkenyl refers to alkenyl groups having from x to y carbon atoms and is meant to include for example, ethenyl, propenyl, 1,3-butadienyl, and so forth.

“Alkynyl” refers to refers to a linear or branched monovalent hydrocarbon radical containing at least one triple bond. The term “alkynyl” may also include those hydrocarbyl groups having other types of bonds, such as a double bond and a triple bond.

“Aryl” refers to an aromatic group of from 3 to 14 carbon atoms and no ring heteroatoms and having a single ring (e.g., phenyl) or multiple condensed (fused) rings (e.g., naphthyl or anthryl). For multiple ring systems, including fused, bridged, and spiro ing systems having aromatic and non-aromatic rings that have no ring heteroatoms, the term “Aryl” applies when the point of attachment is at an aromatic carbon atom (e.g., 5,6,7,8 tetrahydronaphthalene-2-yl is an aryl group as its point of attachment is at the 2-position of the aromatic phenyl ring).

“Cycloalkyl” refers to a saturated or partially saturated cyclic group of from 3 to 14 carbon atoms and no ring heteroatoms and having a single ring or multiple rings including fused, bridged, and spiro ring systems. For multiple ring systems having aromatic and non-aromatic rings that have no ring heteroatoms, the term “cycloalkyl” applies when the point of attachment is at a non-aromatic carbon atom (e.g. 5,6,7,8,-tetrahydronaphthalene-5-yl). The term “cycloalkyl” includes cycloalkenyl groups, such as adamantyl, cyclopropyl, cyclobutyl, cyclopentyl, cyclooctyl, and cyclohexenyl. The term “cycloalkenyl” is sometimes employed to refer to a partially saturated cycloalkyl ring having at least one site of >C═C< ring unsaturation.

“Halo” or “halogen” refers to fluoro, chloro, bromo, and iodo.

“Haloalkyl” refers to substitution of alkyl groups with 1 to 5 or in some embodiments 1 to 3 halo groups.

“Heteroaryl” refers to an aromatic group of from 1 to 14 carbon atoms and 1 to 6 heteroatoms selected from oxygen, nitrogen, and sulfur and includes single ring (e.g. imidazolyl) and multiple ring systems (e.g. benzimidazol-2-yl and benzimidazol-6-yl). For multiple ring systems, including fused, bridged, and spiro ring systems having aromatic and non-aromatic rings, the term “heteroaryl” applies if there is at least one ring heteroatom and the point of attachment is at an atom of an aromatic ring (e.g. 1,2,3,4-tetrahydroquinolin-6-yl and 5,6,7,8-tetrahydroquinolin-3-yl). In some embodiments, the nitrogen and/or the sulfur ring atom(s) of the heteroaryl group are optionally oxidized to provide for the N oxide (N→O), sulfinyl, or sulfonyl moieties. Examples of heteroaryl groups include, but are not limited to, pyridyl, furanyl, thienyl, thiazolyl, isothiazolyl, triazolyl, imidazolyl, imidazolinyl, isoxazolyl, pyrrolyl, pyrazolyl, pyridazinyl, pyrimidinyl, purinyl, phthalazyl, naphthylpryidyl, benzofuranyl, tetrahydrobenzofuranyl, isobenzofuranyl, benzothiazolyl, benzoisothiazolyl, benzotriazolyl, indolyl, isoindolyl, indolizinyl, dihydroindolyl, indazolyl, indolinyl, benzoxazolyl, quinolyl, isoquinolyl, quinolizyl, quianazolyl, quinoxalyl, tetrahydroquinolinyl, isoquinolyl, quinazolinonyl, benzimidazolyl, benzisoxazolyl, benzothienyl, benzopyridazinyl, pteridinyl, carbazolyl, carbolinyl, phenanthridinyl, acridinyl, phenanthrolinyl, phenazinyl, phenoxazinyl, phenothiazinyl, and phthalimidyl.

“Heterocyclic” or “heterocycle” or “heterocycloalkyl” or “heterocyclyl” refers to a saturated or partially saturated cyclic group having from 1 to 14 carbon atoms and from 1 to 6 heteroatoms selected from nitrogen, sulfur, or oxygen and includes single ring and multiple ring systems including fused, bridged, and spiro ring systems. For multiple ring systems having aromatic and/or non-aromatic rings, the terms “heterocyclic”, “heterocycle”, “heterocycloalkyl”, or “heterocyclyl” apply when there is at least one ring heteroatom and the point of attachment is at an atom of a non-aromatic ring (e.g. decahydroquinolin-6-yl). In some embodiments, the nitrogen and/or sulfur atom(s) of the heterocyclic group are optionally oxidized to provide for the N oxide, sulfinyl, sulfonyl moieties. Examples of heterocyclyl groups include, but are not limited to, azetidinyl, tetrahydropyranyl, piperidinyl, N-methylpiperidin-3-yl, piperazinyl, N-methylpyrrolidin-3-yl, 3-pyrrolidinyl, 2-pyrrolidon-1-yl, morpholinyl, thiomorpholinyl, imidazolidinyl, and pyrrolidinyl.

It should be understood that the aforementioned definitions encompass unsubstituted groups, as well as groups substituted with one or more other functional groups as is known in the art. For example, an aryl, heteroaryl, cycloalkyl, or heterocyclyl group may be substituted with from 1 to 8, in some embodiments from 1 to 5, in some embodiments from 1 to 3, and in some embodiments, from 1 to 2 substituents selected from alkyl, alkenyl, alkynyl, alkoxy, acyl, acylamino, acyloxy, amino, quaternary amino, amide, imino, amidino, aminocarbonylamino, amidinocarbonylamino, aminothiocarbonyl, aminocarbonylamino, aminothiocarbonylamino, aminocarbonyloxy, aminosulfonyl, aminosulfonyloxy, aminosulfonylamino, aryl, aryloxy, arylthio, azido, carboxyl, carboxyl ester, (carboxyl ester)amino, (carboxyl ester)oxy, cyano, cycloalkyl, cycloalkyloxy, cycloalkylthio, guanidino, halo, haloalkyl, haloalkoxy, hydroxy, hydroxyamino, alkoxyamino, hydrazino, heteroaryl, heteroaryloxy, heteroarylthio, heterocyclyl, heterocyclyloxy, heterocyclylthio, nitro, oxo, thione, phosphate, phosphonate, phosphinate, phosphonamidate, phosphorodiamidate, phosphoramidate monoester, cyclic phosphoramidate, cyclic phosphorodiamidate, phosphoramidate diester, sulfate, sulfonate, sulfonyl, substituted sulfonyl, sulfonyloxy, thioacyl, thiocyanate, thiol, alkylthio, etc., as well as combinations of such substituents.

“Liquid crystalline polymer” or “liquid crystal polymer” refers to a polymer that can possess a rod-like structure that allows it to exhibit liquid crystalline behavior in its molten state (e.g., thermotropic nematic state). The polymer may contain aromatic units (e.g., aromatic polyesters, aromatic polyesteramides, etc.) so that it is wholly aromatic (e.g., containing only aromatic units) or partially aromatic (e.g., containing aromatic units and other units, such as cycloaliphatic units). The polymer may also be fully crystalline or semi-crystalline in nature.

DETAILED DESCRIPTION

It is to be understood by one of ordinary skill in the art that the present discussion is a description of exemplary embodiments only, and is not intended as limiting the broader aspects of the present invention.

Generally speaking, the present invention is directed to a thermotropic liquid crystalline polymer melt polymerized in the presence of a viscosity modifier that can help increase the “low shear” viscosity of the resulting composition. The increased “low shear” viscosity can minimize drooling of the polymer composition during processing and also allow it to possess a greater melt strength, which facilitates its ability to be processed in a wide variety of applications without losing its physical integrity. Despite having a relatively high “low shear” viscosity, the present inventors have discovered that the viscosity modifier does not substantially increase the “high shear” melt viscosity of the polymer composition. In this regard, the ratio of the “low shear” viscosity to the melt viscosity is generally very high, such as within a range of from about 50 to about 1000, in some embodiments from about 100 to about 800, and in some embodiments, from about 150 to about 500, wherein the low shear viscosity is determined by a parallel plate rheometer at an angular frequency of 0.15 radians per second, a temperature of 350° C., and at a constant strain amplitude of 1%, and the melt viscosity is determined by a capillary rheometer at a temperature of 350° C. and shear rate of 1000 seconds⁻¹. For instance, the polymer composition may have “low shear” complex viscosity of about 3,500 Pa-s or more, in some embodiments about 5,000 Pa-s or more, in some embodiments from about 7,500 to about 100,000 Pa-s, and in some embodiments, from about 10,000 to about 50,000 Pa-s. The polymer composition may likewise have a melt viscosity of about 200 Pa-s or less, in some embodiments about 150 Pa-s or less, in some embodiments from about 0.5 to about 75 Pa-s, and in some embodiments, from about 1 to about 50 Pa-s.

As noted above, the ability to form a polymer composition with the properties noted above is achieved by polymerizing monomeric constituents of the polymer in the presence of a unique viscosity modifier—an aromatic amide oligomer. The aromatic amide oligomer has a molecular weight that is high enough so that it can effectively increase the low shear viscosity of the polymer as it is formed, yet not so high that polymerization is substantially inhibited. In this regard, the oligomer typically has a molecular weight of from about 450 to about 5,000 grams per mole, in some embodiments from about 475 to about 3,000 grams per mole, in some embodiments from about 500 to about 2,500 grams per mole, and in some embodiments, from about 550 to about 1,500 grams per mole.

One benefit of the aromatic amide viscosity modifier is that it is not easily volatized or decomposed, which allows the additive to be processed at relatively high temperatures during the polymerization reaction. Without intending to be limited by theory, it is believed that active hydrogen atoms of the amide functional groups are capable of forming a hydrogen bond with the backbone of liquid crystalline polyesters or polyesteramides. Such hydrogen bonding strengthens the attachment of the oligomer to the liquid crystalline polymer matrix and thus minimizes the likelihood that it becomes volatilized during formation. In this regard, the oligomer generally possesses a high amide functionality so it is capable of undergoing a sufficient degree of hydrogen bonding with the liquid crystalline polymer. The degree of amide functionality for a given molecule may be characterized by its “amide equivalent weight”, which reflects the amount of a compound that contains one molecule of an amide functional group and may be calculated by dividing the molecular weight of the compound by the number of amide groups in the molecule. For example, the aromatic amide oligomer may contain from 2 to 15, in some embodiments from 3 to 12, and in some embodiments, from 4 to 8 amide functional groups per molecule. The amide equivalent weight may likewise be from about 10 to about 1,000 grams per mole or less, in some embodiments from about 50 to about 500 grams per mole, and in some embodiments, from about 100 to about 300 grams per mole.

While providing the benefits noted above, the aromatic amide oligomer does not generally form covalent bonds with the polymer backbone of the liquid crystalline polymer to any appreciable extent so that the mechanical properties of the polymer are not adversely impacted. To help better minimize reactivity, the oligomer typically contains a core formed from one or more aromatic rings (including heteroaromatic). The oligomer may also contain terminal groups formed from one or more aromatic rings and/or cycloalkyl groups. Such an “aromatic” oligomer thus possesses little, if any, reactivity with the base liquid crystalline polymer. For example, one embodiment of such an aromatic amide oligomer is provided below in Formula (I):

wherein,

rings A and B are independently a 6-membered aromatic ring wherein 1 to 3 ring carbon atoms are optionally replaced by nitrogen or oxygen, wherein each nitrogen is optionally oxidized, and wherein rings A and B may be optionally fused or linked to a 5- or 6-membered aryl, heteroaryl, cycloalkyl, or heterocyclyl;

R₅ is halo, haloalkyl, alkyl, alkenyl, aryl, heteroaryl, cycloalkyl, or heterocyclyl;

m is from 0 to 4;

X₁ and X₂ are independently C(O)HN or NHC(O); and

R₁ and R₂ are independently selected from aryl, heteroaryl, cycloalkyl, and heterocyclyl.

In certain embodiments, Rings A and/or B may be selected from the following:

wherein,

m is 0, 1, 2, 3, or 4, in some embodiments m is 0, 1, or 2, in some embodiments m is 0 or 1, and in some embodiments, m is 0; and

R₅ is halo, haloalkyl, alkyl, alkenyl, aryl, heteroaryl, cycloalkyl, or heterocyclyl.

In certain embodiments, the oligomer is a di-functional compound in that Ring B is directly bonded to only two (2) amide groups (e.g., C(O)HN or NHC(O)). In such embodiments, m in Formula (I) may be 0. Of course, in certain embodiments, Ring B may also be directly bonded to three (3) or more amide groups. For example, one embodiment of such a compound is provided by general formula (II):

wherein,

ring A, ring B, R₅, X₁, X₂, R₁, and R₂ are as defined above;

m is from 0 to 3;

X₃ is C(O)HN or NHC(O); and

R₃ is selected from aryl, heteroaryl, cycloalkyl, and heterocyclyl.

Another embodiment of such a compound is provided by general formula (III):

wherein,

ring A, ring B, X₁, X₂, X₃, R₁, R₂, and R₃ are as defined above;

X₄ is C(O)HN or NHC(O); and

R₄ is selected from aryl, heteroaryl, cycloalkyl, and heterocyclyl.

In some embodiments, R₁, R₂, R₃ and/or R₄ in the Formula (II) or Formula (III) may be selected from the following:

wherein,

n is 0, 1, 2, 3, 4, or 5, in some embodiments n is 0, 1, or 2, and in some embodiments, n is 0; and

R₆ is halo, haloalkyl, alkyl, alkenyl, alkynyl, aryl, heteroaryl, cycloalkyl, or heterocyclyl.

In one particular embodiment, the aromatic amide oligomer has the following general formula (IV):

wherein,

X₁, X₂, X₄, and X₅ are independently C(O)HN or NHC(O);

R₅, R₇, R₈, R₁₀, and R₁₁ are independently selected from aryl, heteroaryl, cycloalkyl, and heterocyclyl;

m is from 0 to 4; and

p, q, s, and t are independently from 0 to 5.

For example, in certain embodiments, m, p, and/or q in Formula (IV) may be 0. Likewise, s and/or t may 0. Alternatively, s and/or t may be from 1 to 5. In such embodiments, R₁₀ and/or R₁₁ may be aryl (e.g., phenyl), cycloalkyl (e.g., cyclohexyl), aryl substituted with and/or cycloalkyl substituted with an amide group having the structure: —C(O)R₁₂N— or —NR₁₃C(O)—, wherein R₁₂ and R₁₃ are independently selected from hydrogen, alkyl, alkenyl, alkynyl, aryl, heteroaryl, cycloalkyl, and heterocyclyl. In one particular embodiment, for example, R₁₀ and/or R₁₁ are phenyl substituted with —C(O)HN— or —NHC(O)—. In yet other embodiments, R₁₀ and/or R₁₁ may be heteroaryl (e.g., pyridinyl).

In yet another embodiment, the aromatic amide oligomer has the following general formula (V):

wherein,

X₁, X₂, X₃ X₄, X₅, and X₆ are independently C(O)HN or NHC(O);

R₅, R₇, R₈, R₉, R₁₀, R₁₁, and R₁₄ are independently selected from halo, haloalkyl, alkyl, alkenyl, aryl, heteroaryl, cycloalkyl, and heterocyclyl;

m is from 0 to 3; and

p, q, r, s, t, and v are independently from 0 to 5.

For example, in certain embodiments, m, p, q, and/or r in Formula (V) may be 0. Likewise, s, t, and/or v may be 0. Alternatively, s t, and/or v may be from 1 to 5. In such embodiments, R₁₀, R₁₁, and/or R₁₄ may be aryl (e.g., phenyl), cycloalkyl (e.g., cyclohexyl), aryl substituted with and/or cycloalkyl substituted with an amide group having the structure: —C(O)R₁₂N— or —NR₁₃C(O)—, wherein R₁₂ and R₁₃ are independently selected from hydrogen, alkyl, alkenyl, alkynyl, aryl, heteroaryl, cycloalkyl, and heterocyclyl. In one particular embodiment, for example, R₁₀, R₁₁, and/or R₁₄ are phenyl substituted with —C(O)HN— or —NHC(O)—. In yet other embodiments, R₁₀, R₁₁, and/or R₁₄ may be heteroaryl (e.g., pyridinyl).

Specific embodiments of the aromatic amide oligomer of the present invention are also set forth in the table below:

Cmpd MW # Structure Name (g/mol) A

N1,N4-bis(4- benzamidophenyl) terephthal-amide 554.6 B

N1,N3,N5-tris(4- benzamidophenyl) benzene- 1,3,5-tricarboxamide 792.8 C

N4-phenyl-N1-[4-[[4- (phenylcarbamoyl) benzoyl] amino]phenyl] terephthalamide 554.6 D1

N4-phenyl-N1-[3-[[4- (phenylcarbamoyl) benzoyl] amino]phenyl] terephthalamide 554.6 D2

N1,N3-bis(4- benzamidophenyl) benzene- 1,3-dicarboxamide 554.6 E1

N3-phenyl-N1-[3-[[3- (phenylcarbamoyl) benzoyl] amino]phenyl] benzene-1,3- dicarboxamide 554.6 E2

N1,N3-bis(3- benzamidophenyl) benzene- 1,3-dicarboxamide 554.6 F

N1,N3-bis(4- phenylphenyl)benzene- 1,3-dicarboxamide 468.5 G

N1,N3,N5-tris(3- benzamidophenyl) benzene- 1,3,5-tricarboxamide 792.8

The precursor monomers employed during the formation of the liquid crystalline polymer may generally vary as is known in the art. For example, suitable thermotropic liquid crystalline polymers may include instance, aromatic polyesters, aromatic poly(esteramides), aromatic poly(estercarbonates), aromatic polyamides, etc., and may likewise contain repeating units formed from one or more aromatic or aliphatic hydroxycarboxylic acids, aromatic or aliphatic dicarboxylic acids, aromatic or aliphatic diols, aromatic or aliphatic aminocarboxylic acids, aromatic or aliphatic amines, aromatic or aliphatic diamines, etc., as well as combinations thereof.

Aromatic polyesters, for instance, may be obtained by polymerizing (1) two or more aromatic hydroxycarboxylic acids; (2) at least one aromatic hydroxycarboxylic acid, at least one aromatic dicarboxylic acid, and at least one aromatic diol; and/or (3) at least one aromatic dicarboxylic acid and at least one aromatic diol. Examples of suitable aromatic hydroxycarboxylic acids include, 4-hydroxybenzoic acid; 4-hydroxy-4′-biphenylcarboxylic acid; 2-hydroxy-6-naphthoic acid; 2-hydroxy-5-naphthoic acid; 3-hydroxy-2-naphthoic acid; 2-hydroxy-3-naphthoic acid; 4′-hydroxyphenyl-4-benzoic acid; 3′-hydroxyphenyl-4-benzoic acid; 4′-hydroxyphenyl-3-benzoic acid, etc., as well as alkyl, alkoxy, aryl and halogen substituents thereof. Examples of suitable aromatic dicarboxylic acids include terephthalic acid; isophthalic acid; 2,6-naphthalenedicarboxylic acid; diphenyl ether-4,4′-dicarboxylic acid; 1,6-naphthalenedicarboxylic acid; 2,7 naphthalenedicarboxylic acid; 4,4′-dicarboxybiphenyl; bis(4-carboxyphenyl)ether; bis(4-carboxyphenyl)butane; bis(4-carboxyphenyl)ethane; bis(3-carboxyphenyl)ether; bis(3-carboxyphenyl)ethane, etc., as well as alkyl, alkoxy, aryl and halogen substituents thereof. Examples of suitable aromatic diols include hydroquinone; resorcinol; 2,6-dihydroxynaphthalene; 2,7-dihydroxynaphthalene; 1,6-dihydroxynaphthalene; 4,4′-dihydroxybiphenyl; 3,3′-dihydroxybiphenyl; 3,4′-dihydroxybiphenyl; 4,4′-dihydroxybiphenyl ether; bis(4-hydroxyphenyl)ethane, etc., as well as alkyl, alkoxy, aryl and halogen substituents thereof. In one particular embodiment, the aromatic polyester contains monomer repeat units derived from 4-hydroxybenzoic acid and 2,6-hydroxynaphthoic acid. The monomer units derived from 4-hydroxybenzoic acid may constitute from about 45% to about 85% (e.g., 73%) of the polymer on a mole basis and the monomer units derived from 2,6-hydroxynaphthoic acid may constitute from about 15% to about 55% (e.g., 27%) of the polymer on a mole basis. Such aromatic polyesters are commercially available from Ticona, LLC under the trade designation VECTRA® A. The synthesis and structure of these and other aromatic polyesters may be described in more detail in U.S. Pat. Nos. 4,161,470; 4,473,682; 4,522,974; 4,375,530; 4,318,841; 4,256,624; 4,219,461; 4,083,829; 4,184,996; 4,279,803; 4,337,190; 4,355,134; 4,429,105; 4,393,191; 4,421,908; 4,434,262; and 5,541,240.

Liquid crystalline polyesteramides may likewise be obtained by polymerizing (1) at least one aromatic hydroxycarboxylic acid and at least one aromatic aminocarboxylic acid; (2) at least one aromatic hydroxycarboxylic acid, at least one aromatic dicarboxylic acid, and at least one aromatic amine and/or diamine optionally having phenolic hydroxy groups; and (3) at least one aromatic dicarboxylic acid and at least one aromatic amine and/or diamine optionally having phenolic hydroxy groups. Suitable aromatic amines and diamines may include, for instance, 3-aminophenol; 4-aminophenol; 1,4-phenylenediamine; 1,3-phenylenediamine, etc., as well as alkyl, alkoxy, aryl and halogen substituents thereof. In one particular embodiment, the aromatic polyesteramide contains monomer units derived from 2,6-hydroxynaphthoic acid, terephthalic acid, and 4-aminophenol. The monomer units derived from 2,6-hydroxynaphthoic acid may constitute from about 35% to about 85% of the polymer on a mole basis (e.g., 60%), the monomer units derived from terephthalic acid may constitute from about 5% to about 50% (e.g., 20%) of the polymer on a mole basis, and the monomer units derived from 4-aminophenol may constitute from about 5% to about 50% (e.g., 20%) of the polymer on a mole basis. Such aromatic polyesters are commercially available from Ticona, LLC under the trade designation VECTRA® B. In another embodiment, the aromatic polyesteramide contains monomer units derived from 2,6-hydroxynaphthoic acid, and 4-hydroxybenzoic acid, and 4-aminophenol, as well as other optional monomers (e.g., 4,4′-dihydroxybiphenyl and/or terephthalic acid). The synthesis and structure of these and other aromatic poly(esteramides) may be described in more detail in U.S. Pat. Nos. 4,339,375; 4,355,132; 4,351,917; 4,330,457; 4,351,918; and 5,204,443.

Regardless of their particular constituents, the liquid crystalline polymers may be prepared by introducing the appropriate monomer(s) (e.g., aromatic hydroxycarboxylic acid, aromatic dicarboxylic acid, aromatic diol, aromatic amine, aromatic diamine, etc.) into a reactor vessel to initiate a polycondensation reaction. The particular conditions and steps employed in such reactions are well known, and may be described in more detail in U.S. Pat. No. 4,161,470 to Calundann; U.S. Pat. No. 5,616,680 to Linstid, III, et al.; U.S. Pat. No. 6,114,492 to Linstid, III, et al.; U.S. Pat. No. 6,514,611 to Shepherd, et al.; and WO 2004/058851 to Waggoner, which are incorporated herein in their entirety by reference thereto for all relevant purposes. The vessel employed for the reaction is not especially limited, although it is typically desired to employ one that is commonly used in reactions of high viscosity fluids. Examples of such a reaction vessel may include a stirring tank-type apparatus that has an agitator with a variably-shaped stirring blade, such as an anchor type, multistage type, spiral-ribbon type, screw shaft type, etc., or a modified shape thereof. Further examples of such a reaction vessel may include a mixing apparatus commonly used in resin kneading, such as a kneader, a roll mill, a Banbury mixer, etc.

If desired, the reaction may proceed through the acetylation of the monomers as referenced above and known the art. This may be accomplished by adding an acetylating agent (e.g., acetic anhydride) to the monomers. Acetylation is generally initiated at temperatures of about 90° C. During the initial stage of the acetylation, reflux may be employed to maintain vapor phase temperature below the point at which acetic acid byproduct and anhydride begin to distill. Temperatures during acetylation typically range from between 90° C. to 150° C., and in some embodiments, from about 110° C. to about 150° C. If reflux is used, the vapor phase temperature typically exceeds the boiling point of acetic acid, but remains low enough to retain residual acetic anhydride. For example, acetic anhydride vaporizes at temperatures of about 140° C. Thus, providing the reactor with a vapor phase reflux at a temperature of from about 110° C. to about 130° C. is particularly desirable. To ensure substantially complete reaction, an excess amount of acetic anhydride may be employed. The amount of excess anhydride will vary depending upon the particular acetylation conditions employed, including the presence or absence of reflux. The use of an excess of from about 1 to about 10 mole percent of acetic anhydride, based on the total moles of reactant hydroxyl groups present is not uncommon.

Acetylation may occur in a separate reactor vessel, or it may occur in situ within the polymerization reactor vessel. When separate reactor vessels are employed, one or more of the monomers may be introduced to the acetylation reactor and subsequently transferred to the polymerization reactor. Likewise, one or more of the monomers may also be directly introduced to the reactor vessel without undergoing pre-acetylation.

The aromatic amide oligomer of the present invention is typically added to the polymerization apparatus. Although it may be introduced at any time, it is normally desired to apply the oligomer before melt polymerization has been initiated, and typically in conjunction with the precursor monomers for the liquid crystalline polymer. The relative amount of the aromatic amide oligomer added to the reaction mixture may be selected to help achieve a balance between high shear viscosity and mechanical properties. More particularly, high oligomer contents can result in low “high shear” viscosity, but too high of a content may reduce the viscosity to such an extent that the oligomer adversely impacts the melt strength of the reaction mixture. In most embodiments, for example, the aromatic amide oligomer or mixtures thereof may be employed in an amount of from about 0.1 to about 5 parts, in some embodiments from about 0.2 to about 4 parts, and in some embodiments, from about 0.3 to about 1.5 parts by weight relative to 100 parts by weight of the reaction mixture. The aromatic amide oligomers may, for example, constitute from about 0.1 wt. % to about 5 wt. %, in some embodiments from about 0.2 wt % to about 4 wt. %, and in some embodiments, from about 0.3 wt. % to about 1.5 wt. % of the reaction mixture. Liquid crystalline polymers may likewise constitute from about 95 wt. % to about 99.9 wt %, in some embodiments from about 96 wt. % to about 98.8 wt. %, and in some embodiments, from about 98.5 wt. % to about 99.7 wt. % of the reaction mixture. While referred to in terms of the reaction mixture, it should also be understood that the ratios and weight percentages may also be applicable to the final polymer composition. That is, the parts by weight of the oligomer relative to 100 parts by weight of liquid crystalline polymer and the percentage of the oligomer in the final polymer composition may be within the ranges noted above.

In addition to the monomers, oligomer, and optional acetylating agents, other components may also be included within the reaction mixture to help facilitate polymerization. For instance, a catalyst may be optionally employed, such as metal salt catalysts (e.g., magnesium acetate, tin(I) acetate, tetrabutyl titanate, lead acetate, sodium acetate, potassium acetate, etc.) and organic compound catalysts (e.g., N-methylimidazole). Such catalysts are typically used in amounts of from about 50 to about 500 parts per million based on the total weight of the recurring unit precursors. When separate reactors are employed, it is typically desired to apply the catalyst to the acetylation reactor rather than the polymerization reactor, although this is by no means a requirement.

The reaction mixture is generally heated to an elevated temperature within the polymerization reactor vessel to initiate melt polycondensation of the reactants. Polycondensation may occur, for instance, within a temperature range of from about 210° C. to about 400° C., and in some embodiments, from about 250° C. to about 350° C. For instance, one suitable technique for forming an aromatic polyester may include charging precursor monomers (e.g., 4-hydroxybenzoic acid and 2,6-hydroxynaphthoic acid), aromatic amide oligomer, and acetic anhydride into the reactor, heating the mixture to a temperature of from about 90° C. to about 150° C. to acetylize a hydroxyl group of the monomers (e.g., forming acetoxy), and then increasing the temperature to a temperature of from about 210° C. to about 400° C. to carry out melt polycondensation. As the final polymerization temperatures are approached, volatile byproducts of the reaction (e.g., acetic acid) may also be removed so that the desired molecular weight may be readily achieved. The reaction mixture is generally subjected to agitation during polymerization to ensure good heat and mass transfer, and in turn, good material homogeneity. The rotational velocity of the agitator may vary during the course of the reaction, but typically ranges from about 10 to about 100 revolutions per minute (“rpm”), and in some embodiments, from about 20 to about 80 rpm. To build molecular weight in the melt, the polymerization reaction may also be conducted under vacuum, the application of which facilitates the removal of volatiles formed during the final stages of polycondensation. The vacuum may be created by the application of a suctional pressure, such as within the range of from about 5 to about 30 pounds per square inch (“psi”), and in some embodiments, from about 10 to about 20 psi.

Following melt polymerization, the molten polymer may be discharged from the reactor, typically through an extrusion orifice fitted with a die of desired configuration, cooled, and collected. Commonly, the melt is discharged through a perforated die to form strands that are taken up in a water bath, pelletized and dried. The resin may also be in the form of a strand, granule, or powder. While unnecessary, it should also be understood that a subsequent solid phase polymerization may be conducted to further increase molecular weight. When carrying out solid-phase polymerization on a polymer obtained by melt polymerization, it is typically desired to select a method in which the polymer obtained by melt polymerization is solidified and then pulverized to form a powdery or flake-like polymer, followed by performing solid polymerization method, such as a heat treatment in a temperature range of 200° C. to 350° C. under an inert atmosphere (e.g., nitrogen).

Regardless of the particular method employed, the resulting liquid crystalline polymer typically may have a high number average molecular weight (M_(n)) of about 2,000 grams per mole or more, in some embodiments from about 4,000 grams per mole or more, and in some embodiments, from about 5,000 to about 30,000 grams per mole. Of course, it is also possible to form polymers having a lower molecular weight, such as less than about 2,000 grams per mole, using the method of the present invention. The intrinsic viscosity of the polymer composition, which is generally proportional to molecular weight, may also be relatively high. For example, the intrinsic viscosity may be about 4 deciliters per gram (“dL/g”) or more, in some embodiments about 5 dL/g or more, in some embodiments from about 6 to about 20 dL/g, and in some embodiments from about 7 to about 15 dL/g. Intrinsic viscosity may be determined in accordance with ISO-1628-5 using a 50/50 (v/v) mixture of pentafluorophenol and hexafluoroisopropanol, as described in more detail below.

The melting point of the polymer composition may also range from about 250° C. to about 400° C., in some embodiments from about 270° C. to about 380° C., and in some embodiments, from about 300° C. to about 360° C. Likewise, the crystallization temperature may range from about 200° C. to about 400° C., in some embodiments from about 250° C. to about 350° C., and in some embodiments, from about 280° C. to about 320° C. The melting and crystallization temperatures may be determined as is well known in the art using differential scanning calorimetry (“DSC”), such as determined by ISO Test No. 11357.

If desired, the resulting polymer composition may also be combined with a wide variety of other types of components to form a filled composition. For example, a filler material may be incorporated with the polymer composition to enhance strength. A filled composition can include a filler material such as a fibrous filler and/or a mineral filler and optionally one or more additional additives as are generally known in the art.

Mineral fillers may, for instance, be employed in the polymer composition to help achieve the desired mechanical properties and/or appearance. When employed, mineral fillers typically constitute from about 5 wt. % to about 60 wt. %, in some embodiments from about 10 wt. % to about 55 wt. %, and in some embodiments, from about 20 wt. % to about 50 wt. % of the polymer composition. Clay minerals may be particularly suitable for use in the present invention. Examples of such clay minerals include, for instance, talc (Mg₃Si₄O₁₀(OH)₂), halloysite (Al₂Si₂O₅(OH)₄), kaolinite (Al₂Si₂O₅(OH)₄), illite ((K,H₃O)(Al,Mg,Fe)₂(Si,Al)₄O₁₀[(OH)₂,(H₂O)]), montmorillonite (Na,Ca)_(0.33)(Al,Mg)₂Si₄O₁₀(OH)₂.4(H₂O), vermiculite ((MgFe,Al)₃(Al,SO₄O₁₀(OH)₂. 4H₂O), palygorskite ((Mg,Al)₂Si₄O₁₀(OH).4(H₂O)), pyrophyllite (Al₂Si₄O₁₀(OH)₂), etc., as well as combinations thereof. In lieu of, or in addition to, clay minerals, still other mineral fillers may also be employed. For example, other suitable silicate fillers may also be employed, such as calcium silicate, aluminum silicate, mica, diatomaceous earth, wollastonite, and so forth. Mica, for instance, may be particularly suitable. There are several chemically distinct mica species with considerable variance in geologic occurrence, but all have essentially the same crystal structure. As used herein, the term “mica” is meant to generically include any of these species, such as muscovite (KAl₂(AlSi₃)O₁₀(OH)₂), biotite (K(Mg,Fe)₃(AlSi₃)O₁₀(OH)₂), phlogopite (KMg₃(AlSi₃)O₁₀(OH)₂), lepidolite (K(Li,Al)₂₋₃(AlSi₃)O₁₀(OH)₂), glauconite (K,Na)(Al,Mg,Fe)₂(Si,Al)₄O₁₀(OH)₂), etc., as well as combinations thereof.

Fibers may also be employed as a filler material to further improve the mechanical properties. Such fibers generally have a high degree of tensile strength relative to their mass. For example, the ultimate tensile strength of the fibers (determined in accordance with ASTM D2101) is typically from about 1,000 to about 15,000 Megapascals (“MPa”), in some embodiments from about 2,000 MPa to about 10,000 MPa, and in some embodiments, from about 3,000 MPa to about 6,000 MPa. To help maintain an insulative property, which is often desirable for use in electronic components, the high strength fibers may be formed from materials that are also generally insulative in nature, such as glass, ceramics (e.g., alumina or silica), aramids (e.g., Kevlar® marketed by E. I. duPont de Nemours, Wilmington, Del.), polyolefins, polyesters, etc., as well as mixtures thereof. Glass fibers are particularly suitable, such as E-glass, Aglass, C-glass, D-glass, AR-glass, R-glass, S1-glass, S2-glass, etc., and mixtures thereof.

The volume average length of the fibers may be from about 50 to about 400 micrometers, in some embodiments from about 80 to about 250 micrometers, in some embodiments from about 100 to about 200 micrometers, and in some embodiments, from about 110 to about 180 micrometers. The fibers may also have a narrow length distribution. That is, at least about 70% by volume of the fibers, in some embodiments at least about 80% by volume of the fibers, and in some embodiments, at least about 90% by volume of the fibers have a length within the range of from about 50 to about 400 micrometers, in some embodiments from about 80 to about 250 micrometers, in some embodiments from about 100 to about 200 micrometers, and in some embodiments, from about 110 to about 180 micrometers. The fibers may also have a relatively high aspect ratio (average length divided by nominal diameter) to help improve the mechanical properties of the resulting polymer composition. For example, the fibers may have an aspect ratio of from about 2 to about 50, in some embodiments from about 4 to about 40, and in some embodiments, from about 5 to about 20 are particularly beneficial. The fibers may, for example, have a nominal diameter of about 10 to about 35 micrometers, and in some embodiments, from about 15 to about 30 micrometers.

The relative amount of the fibers in the filled polymer composition may also be selectively controlled to help achieve the desired mechanical properties without adversely impacting other properties of the composition, such as its flowability. For example, the fibers may constitute from about 2 wt. % to about 40 wt. %, in some embodiments from about 5 wt. % to about 35 wt. %, and in some embodiments, from about 6 wt. % to about 30 wt. % of the polymer composition. Although the fibers may be employed within the ranges noted above, small fiber contents may be employed while still achieving the desired mechanical properties. For example, the fibers can be employed in small amounts such as from about 2 wt. % to about 20 wt. %, in some embodiments, from about 5 wt. % to about 16 wt. %, and in some embodiments, from about 6 wt. % to about 12 wt. %.

Still other additives that can be included in the composition may include, for instance, antimicrobials, pigments (e.g., carbon black), antioxidants, stabilizers, surfactants, waxes, solid solvents, and other materials added to enhance properties and processability. Lubricants, for instance, may be employed in the polymer composition. Examples of such lubricants include fatty acids esters, the salts thereof, esters, fatty acid amides, organic phosphate esters, and hydrocarbon waxes of the type commonly used as lubricants in the processing of engineering plastic materials, including mixtures thereof. Suitable fatty acids typically have a backbone carbon chain of from about 12 to about 60 carbon atoms, such as myristic acid, palmitic acid, stearic acid, arachic acid, montanic acid, octadecinic acid, parinric acid, and so forth. Suitable esters include fatty acid esters, fatty alcohol esters, wax esters, glycerol esters, glycol esters and complex esters. Fatty acid amides include fatty primary amides, fatty secondary amides, methylene and ethylene bisamides and alkanolamides such as, for example, palmitic acid amide, stearic acid amide, oleic acid amide, N,N′-ethylenebisstearamide and so forth. Also suitable are the metal salts of fatty acids such as calcium stearate, zinc stearate, magnesium stearate, and so forth; hydrocarbon waxes, including paraffin waxes, polyolefin and oxidized polyolefin waxes, and microcrystalline waxes. Particularly suitable lubricants are acids, salts, or amides of stearic acid, such as pentaerythritol tetrastearate, calcium stearate, or N,N′-ethylenebisstearamide. When employed, the lubricant(s) typically constitute from about 0.05 wt. % to about 1.5 wt. %, and in some embodiments, from about 0.1 wt. % to about 0.5 wt. % (by weight) of the polymer composition.

The polymer composition of the present invention may be employed in a wide variety of applications as is known in the art, such as blow molding, injection molding, rotational molding, sheet extrusion, thermoforming, etc. Due to its relatively high “low shear” viscosity and associated high degree of melt strength, the composition is particularly well suited for applications that involve the formation of a thin, sheet-like material or film. In certain embodiments, for example, the composition may be formed into a film and then “thermoformed” into the desired shape and/or size of the final product. The film may be prepared using any known technique, such as with a tubular trapped bubble film process, flat or tube cast film process, slit die flat cast film process, etc. Regardless of the manner in which it is formed, the film may be “thermoformed” by heating the film to a certain temperature so that it becomes flowable, shaping the film within a mold, and then trimming the shaped film to create the desired product. The product may, for example, be a package, container, tray (e.g., for a food product), electrical connector, circuit, bottle, pouch, cup, tub, pail, jar, box, etc.

The present invention may be better understood with reference to the following examples.

Test Methods

Melt Viscosity:

The melt viscosity (Pa-s) was determined in accordance with ISO Test No. 11443 at 350° C. and at a shear rate of 400 s⁻¹ and 1000 s⁻¹ using a Dynisco 7001 capillary rheometer. The rheometer orifice (die) had a diameter of 1 mm, length of 20 mm, L/D ratio of 20.1, and an entrance angle of 180°. The diameter of the barrel was 9.55 mm+0.005 mm and the length of the rod was 233.4 mm.

Complex Viscosity:

The complex viscosity is used herein as an estimate for the “low shear” viscosity of the polymer composition at low frequencies. Complex viscosity is a frequency-dependent viscosity, determined during forced harmonic oscillation of shear stress at angular frequencies of 0.15 and 500 radians per second. Measurements were determined at a constant temperature of 350° C. and at a constant strain amplitude of 1% using an ARES-G2 rheometer (TA Instruments) with a parallel plate configuration (25 mm plate diameter).

Intrinsic Viscosity:

The intrinsic viscosity (“IV”) may be measured in accordance with ISO-1628-5 using a 50/50 (v/v) mixture of pentafluorophenol and hexafluoroisopropanol. Each sample was prepared in duplicate by weighing about 0.02 grams into a 22 mL vial. 10 mL of pentafluorophenol (“PFP”) was added to each vial and the solvent. The vials were placed in a heating block set to 80° C. overnight. The following day 10 mL of hexafluoroisopropanol (“HFIP”) was added to each vial. The final polymer concentration of each sample was about 0.1%. The samples were allowed to cool to room temperature and analyzed using a PolyVisc automatic viscometer.

Melting and Crystallization Temperatures:

The melting temperature (“Tm”) and crystallization temperature (“Tc”) were determined by differential scanning calorimetry (“DSC”) as is known in the art. The melting temperature is the differential scanning calorimetry (DSC) peak melt temperature as determined by ISO Test No. 11357. The crystallization temperature is determined from the cooling exotherm in the cooling cycle. Under the DSC procedure, samples were heated and cooled at 20° C. per minute as stated in ISO Standard 10350 using DSC measurements conducted on a TA Q2000 Instrument.

Synthesis of N1,N4-bis(4-benzamidophenyl)terephthalamide Compound A

The synthesis of Compound A from terephthaloyl chloride and 4-aminobenzanilide can be performed according to the following scheme:

The experimental setup consisted of a 1 L glass beaker equipped with a glass rod stirrer coupled with an overhead mechanical stirrer. 4-aminobenzanilide (20.9 g) was dissolved in warm DMAc (250 mL) (alternatively N-methylpyrrolidone can also be used). Terephthaloyl chloride (10 g) was added to the stirred solution of the diamine maintained at 40-50° C., upon the addition of the acid chloride the reaction temperature increased from 50° C. to 80° C. After the addition of the acid chloride was completed, the reaction mixture was warmed to 70-80° C. and maintained at that temperature for about three hours and allowed to rest overnight at room temperature. The product was then isolated by the addition of water (500 mL) followed by vacuum filtration followed by washing with hot water (1 L). The product was then dried in a vacuum oven at 150° C. for about 6-8 hours, to give a pale yellow colored solid (yield ca. 90%). The melting point by DSC was 462° C.

Synthesis of N1,N3,N5-tris(4-benzamidophenyl)benzene-1,3,5-tricarboxamide Compound B

The synthesis of Compound B from trimesoyl chloride and 4-benzoanilide may be performed according to the following scheme:

The experimental set up consisted of a 2 L glass beaker equipped with a glass rod stirrer coupled with an overhead mechanical stirrer. Trimesoyl chloride (83.37 g) was dissolved in DMAc (1 L) at room temperature. 4-aminobenzanilide (200 g) was dissolved in DMAc (1 L). The amine solution was gradually added to the acid chloride solution over a period of 15 minutes, and the reaction mixture was then stirred and the temperature increased to 90° C. for about 3 hours. The mixture was allowed to rest overnight at room temperature. The product was recovered by precipitation through the addition of 1.5 L of distilled water, which was followed by was vacuum filtration using a filter paper and a Buchner funnel. The crude product was then washed with acetone (2 L) and washed again with hot water (2 L). The product was then air dried over night at room temperature and then was dried in a vacuum oven 150° C. for 4 to 6 hours. The product (291 g) was a bright yellow solid. No melting point was detected. The Proton NMR characterization for the compound is shown in FIG. 1.

Synthesis of N1,N3-bis(4-benzamidophenyl)benzene-1,3-dicarboxamide Compound D2

Although not tested in the Examples below, Compound D2 was nevertheless synthesized from 1,3-phenylene diamine, terephthaloyl chloride, and aniline according to the following scheme:

The experimental setup consisted of a 500 mL glass beaker equipped with a magnetic stirrer. 1,4 phenylene diamine (20 g) was dissolved in warm NMP (200 mL) at 40° C. Benzoyl chloride (26.51 g) was added drop wise to a stirred solution of the diamine over a period of 30 minutes. After the addition of the benzoyl chloride was completed, the reaction mixture was warmed to 70-80° C. and then allowed to cool to 50° C. After cooling to the desired temperature, isophthaloyl chloride (18.39 g) was added in small portions such that the temperature of the reaction mixture did not increase above 70° C. The mixture was then stirred for additional one (1) hour at 70° C., and was allowed to rest overnight at room temperature. The product was recovered by addition of water (200 mL) to the reaction mixture, followed by filtration and washing with hot water (500 mL). The product was then dried in a vacuum oven at 150° C. for about 6-8 hours to give a pale yellow colored solid (yield ca. 90%). The melting point by DSC was 329° C. The Proton NMR characterization for the compound is also shown in FIG. 2.

Synthesis of N1,N3-bis(3-benzamidophenyl)benzene-1,3-dicarboxamide Compound E2

Although not tested in the Examples below, Compound E2 was nevertheless synthesized from 1,3-phenylene diamine, isophthaloyl chloride, and aniline according to the following scheme:

The experimental setup consisted of a 500 mL glass beaker equipped with a magnetic stirrer. 1,3 phenylene diamine (20 g) was dissolved in warm DMAc (200 mL) at 40° C. Benzoyl chloride (26.51 g) was added drop wise to a stirred solution of the diamine over a period of 30 minutes. After the addition of the benzoyl chloride was completed, the reaction mixture was warmed to 70-80° C. and allowed to cool to 50° C. After cooling to the desired temperature, isophthaloyl chloride (18.39 g) was added in small portions such that the temperature of the reaction mixture did not increase above 70° C. The mixture was then stirred for additional one hour at 70° C., and was allowed to rest overnight at room temperature. The product was recovered by addition of water (200 mL) to the reaction mixture, followed by filtration and washing with hot water (500 mL). The product was then dried in a vacuum oven at 150° C. for about 6-8 hours to give a pale yellow colored solid (yield ca. 90%). The Proton NMR characterization for the compound is also shown in FIG. 3.

Synthesis of N1,N3,N5-tris(3-benzamidophenyl)benzene-1,3,5-tricarboxamide Compound G

Although not tested in these examples, the synthesis of Compound D from trimesoyl chloride, benzoyl chloride and 1,3-phenylene diamine can be performed according to the following scheme:

The experimental set up consisted of a 1 L glass beaker equipped with a glass rod stirrer coupled with an overhead mechanical stirrer. 1, 3 phenylene diamine (20 g) was dissolved in warm dimethyl acetamide (200 mL) (alternatively N-methylpyrrolidone can also be used) and maintained at 45° C. Next benzoyl chloride (26.51 g) was slowly added drop wise over a period of 1.5 to 2 hours, to the amine solution with constant stirring. The rate of addition of the benzoyl chloride was maintained such that the reaction temperature was maintained less than 60° C. After complete addition of the benzoyl chloride, the reaction mixture was gradually warmed to 85-90° C. and then allowed to cool to around 45-50° C. At this point, trimesoyl chloride (16.03 g) was gradually added to the reaction mixture such that the exotherm did not increase the reaction temperature above 60° C. After complete addition of the trimesoyl chloride, the reaction mixture was allowed to stir for additional 45 minutes, after which the reaction temperature was increased to 90° C. for about 30 minutes and then was cooled to room temperature. The mixture was allowed to rest overnight at room temperature. The product was recovered by precipitation through the addition of 1.5 L of distilled water, which was followed by was vacuum filtration using a filter paper and a Buchner funnel. The crude product was then washed with acetone (250 mL) and washed again with hot water (500 mL). The product (yield: ca. 90%) was then air dried over night at room temperature and then was dried in a vacuum oven 150° C. for 4 to 6 hours. The product was a pale tan solid.

The Proton NMR characterization was as follows: ¹H NMR (400 MHz d₆-DMSO): 10.68 (s, 3H, CONH), 10.3 (s, 3H, CONH), 8.74 (s, 3H, central Ar), 8.1 (d, 3H, m-phenylene Ar), 7.9 (d, 6H, ortho-ArH), 7.51 (m, 15H, meta-para-ArH and 6H, m-phenylene Ar) and 7.36 (m, 3H, m-phenylene Ar).

Example 1

A 2 L flask was charged with 4-hydroxybenzoic acid (432.3 g), 2,6-hydroxynaphthoic acid (47 g), terephthalic acid (134.6 g), 4,4′-biphenol (104.3 g), acetominophen (37.8 g), and 33 mg of potassium acetate. The flask was equipped with C-shaped stirrer, a thermal couple, a gas inlet, and distillation head. The flask was placed under a low nitrogen purge and acetic anhydride (99.7% assay, 501.5 g) was added. The milky-white slurry was agitated at 75 rpm and heated to 140° C. over the course of 95 minutes using a fluidized sand bath. After this time, the mixture was then gradually heated to 350° C. steadily over 290 minutes. Reflux was seen once the reaction exceeded 140° C. and the overhead temperature increased to approximately 115° C. as acetic acid byproduct was removed from the system. During the heating, the mixture grew yellow and slightly more viscous and the vapor temperature gradually dropped to 90° C. Once the mixture had reached 350° C., the nitrogen flow was stopped. The flask was evacuated below 20 psi and the agitation slowed to 30 rpm over the course of 45 minutes. As the time under vacuum progressed, the mixture grew viscous. After 84 minutes, the final viscosity target was reached as gauged by the strain on the agitator motor (torque value of 31 units). The reaction was then stopped by releasing the vacuum and stopping the heat flow to the reactor. The flask was cooled and then polymer was recovered as a solid, dense yellow-brown plug. Sample for analytical testing was obtained by mechanical size reduction.

Example 2

A 2 L flask was charged with HBA (432.3 g), HNA (47 g), TA (134.6 g), BP (104.3 g), APAP (37.8 g), 33 mg of potassium acetate, and 19.65 g of N1, N4-diphenylterephthalamide, which has the following structure:

The flask was equipped with C-shaped stirrer, a thermal couple, a gas inlet, and distillation head. The flask was placed under a low nitrogen purge and acetic anhydride (99.7% assay, 501.5 g) was added. The milky-white slurry was agitated at 75 rpm and heated to 140° C. over the course of 95 minutes using a fluidized sand bath. After this time, the mixture was then gradually heated to 350° C. steadily over 290 minutes. Reflux was seen once the reaction exceeded 140° C. and the overhead temperature increased to approximately 115° C. as acetic acid byproduct was removed from the system. During the heating, the mixture grew yellow and slightly more viscous and the vapor temperature gradually dropped to 90° C. Once the mixture had reached 350° C., the nitrogen flow was stopped. The flask was evacuated below 20 psi and the agitation slowed to 30 rpm over the course of 45 minutes. As the time under vacuum progressed, the mixture grew viscous. After 84 minutes, the reaction was stopped, no torque was observed. The reaction was then stopped by releasing the vacuum and stopping the heat flow to the reactor. The flask was cooled and then polymer was recovered as a solid, dense yellow-brown plug. Sample for analytical testing was obtained by mechanical size reduction.

Example 3

A 2 L flask was charged with HBA (432.3 g), HNA (47 g), TA (134.6 g), BP (104.3 g), APAP (37.8 g), 33 mg potassium acetate, and 19.65 g of N1,N3,N5-triphenylbenzene-1,3,5-tricarboxamide, which has the following structure:

The flask was equipped with C-shaped stirrer, a thermal couple, a gas inlet, and distillation head. The flask was placed under a low nitrogen purge and acetic anhydride (99.7% assay, 501.5 g) was added. The milky-white slurry was agitated at 75 rpm and heated to 140° C. over the course of 95 minutes using a fluidized sand bath. After this time, the mixture was then gradually heated to 350° C. steadily over 290 minutes. Reflux was seen once the reaction exceeded 140° C. and the overhead temperature increased to approximately 115° C. as acetic acid byproduct was removed from the system. During the heating, the mixture grew yellow and slightly more viscous and the vapor temperature gradually dropped to 90° C. Once the mixture had reached 350° C., the nitrogen flow was stopped. The flask was evacuated below 20 psi and the agitation slowed to 30 rpm over the course of 45 minutes. As the time under vacuum progressed, the mixture grew viscous. After 84 minutes, the reaction was stopped, no torque was observed. The reaction was then stopped by releasing the vacuum and stopping the heat flow to the reactor. The flask was cooled and then polymer was recovered as a solid, dense yellow-brown plug. Sample for analytical testing was obtained by mechanical size reduction.

Example 4

A 2 L flask was charged with HBA (432.3 g), HNA (47 g), TA (134.6 g), BP (104.3 g), APAP (37.8 g) and Compound A (19.65 g) and 33 mg of potassium acetate. The flask was equipped with C-shaped stirrer, a thermal couple, a gas inlet, and distillation head. The flask was placed under a low nitrogen purge and acetic anhydride (99.7% assay, 501.5 g) was added. The milky-white slurry was agitated at 75 rpm and heated to 140° C. over the course of 95 minutes using a fluidized sand bath. After this time, the mixture was then gradually heated to 350° C. steadily over 290 minutes. Reflux was seen once the reaction exceeded 140° C. and the overhead temperature increased to approximately 115° C. as acetic acid byproduct was removed from the system. During the heating, the mixture grew yellow and slightly more viscous and the vapor temperature gradually dropped to 90° C. Once the mixture had reached 350° C., the nitrogen flow was stopped. The flask was evacuated below 20 psi and the agitation slowed to 30 rpm over the course of 45 minutes. As the time under vacuum progressed, the mixture grew viscous. After 84 minutes, the reaction was stopped, no torque was observed. The reaction was then stopped by releasing the vacuum and stopping the heat flow to the reactor. The flask was cooled and then polymer was recovered as a solid, dense yellow-brown plug. Sample for analytical testing was obtained by mechanical size reduction.

Example 5

A 2 L flask was charged with HBA (432.3 g), HNA (47 g), TA (134.6 g), BP (104.3 g), APAP (37.8 g) and Compound B (19.65 g) and 33 mg of potassium acetate. The flask was equipped with C-shaped stirrer, a thermal couple, a gas inlet, and distillation head. The flask was placed under a low nitrogen purge and acetic anhydride (99.7% assay, 501.5 g) was added. The milky-white slurry was agitated at 75 rpm and heated to 140° C. over the course of 95 minutes using a fluidized sand bath. After this time, the mixture was then gradually heated to 350° C. steadily over 290 minutes. Reflux was seen once the reaction exceeded 140° C. and the overhead temperature increased to approximately 115° C. as acetic acid byproduct was removed from the system. It was observed that there were fewer residues in the distillate as compared to the analogous run described in Example 1. During the heating, the mixture grew yellow and slightly more viscous and the vapor temperature gradually dropped to 90° C. Once the mixture had reached 350° C., the nitrogen flow was stopped. The flask was evacuated below 20 psi and the agitation slowed to 30 rpm over the course of 45 minutes. As the time under vacuum progressed, the mixture grew viscous. After 84 minutes, the final viscosity target was reached as gauged by the strain on the agitator motor (torque value of 71 units). The reaction was then stopped by releasing the vacuum and stopping the heat flow to the reactor. The flask was cooled and then polymer was recovered as a solid, dense yellow-brown plug. Sample for analytical testing was obtained by mechanical size reduction.

The thermal properties of the polymers of Examples 1-5 were tested as described above. The results are set forth below.

Complex Complex Ratio of MV at MV at Viscosity Viscosity CV (0.15 rad/s) Tm IV 1000 s⁻¹ 400 s⁻¹ (Pa * s), (Pa * s), to Example Additive (° C.) Tc (° C.) (dL/g) (Pa * s) (Pa*s) 0.15 rad/s 500 rad/s MV (1000 s⁻¹) 1 — 343.7 290.8 7.6 79.6 129.0 3,310 116 41.6 2 N1,N4-diphenyl- 320.6 280.7 5.4 4.6 7.0 31 2 6.8 terephthalamide 3 N1,N3,N5- 314.2 268.3 2.6 7.2 9.3 68 6 9.4 triphenyl-benzene- 1,3,5- tricarboxamide 4 A 340.3 290.3 6.5 43.9 63.5 10,900 75 248.3 5 B 343.1 287.1 6.1 117.6 183.4 39,779 332 338.3

As indicated, the use of Compounds A and B in Examples 4-5 resulted in a significant increase in the complex viscosity at frequencies of 0.15 and 500 rad/s. Other frequencies were also tested, the results of which are shown in FIG. 4.

Example 6

A first sample (Sample 1) was formed. A 2 L flask was charged with 4-hydroxybenzoic acid (415.7 g), 2,6-hydroxynaphthoic acid (32 g), terephthalic acid (151.2 g), 4,4′-biphenol (122.9 g), acetominophen (37.8 g), and 50 mg of potassium acetate. The flask was equipped with C-shaped stirrer, a thermal couple, a gas inlet, and distillation head. The flask was placed under a low nitrogen purge and acetic anhydride (99.7% assay, 497.6 g) was added. The milky-white slurry was agitated at 75 rpm and heated to 140° C. over the course of 95 minutes using a fluidized sand bath. After this time, the mixture was then gradually heated to 360° C. steadily over 300 minutes. Reflux was seen once the reaction exceeded 140° C. and the overhead temperature increased to approximately 115° C. as acetic acid byproduct was removed from the system. During the heating, the mixture grew yellow and slightly more viscous and the vapor temperature gradually dropped to 90° C. Once the mixture had reached 360° C., the nitrogen flow was stopped. The flask was evacuated below 20 psi and the agitation slowed to 30 rpm over the course of 45 minutes. As the time under vacuum progressed, the mixture grew viscous. After 72 minutes, the final viscosity target was reached as gauged by the strain on the agitator motor (torque value of 30 units). The reaction was then stopped by releasing the vacuum and stopping the heat flow to the reactor. The flask was cooled and then polymer was recovered as a solid, dense yellow-brown plug. Sample for analytical testing was obtained by mechanical size reduction.

A second sample (Sample 2) was formed as described for Sample 1, except that 19.65 grams of Compound A was also introduced into the reactor. It was observed that there were fewer residues in the distillate as compared to Sample 1. The reaction was stopped after 72 minutes—no torque was observed on the agitator motor.

A third sample (Sample 3) was formed as described for Sample 1, except that 18.7 grams of Compound B was also introduced into the reactor. It was observed that there were fewer residues in the distillate as compared to Sample 1. The reaction was stopped after 72 minutes—a torque value of 50 units was observed on the agitator motor.

The thermal properties of the melt polymerized polymers of Samples 1-3 were tested as described above. The results are set forth below in the following table.

MV at MV at Tc 1000 s⁻¹ 400 s⁻¹ Sample Additive Tm (° C.) (° C.) IV (dL/g) (Pa * s) (Pa * s) 1 — 361.6 301.8 8.4 75.7 118.2 2 A 350.6 299.3 5.3 46.8 70.7 3 B 343.0 284.7 5.0 137.8 230.1

These and other modifications and variations of the present invention may be practiced by those of ordinary skill in the art, without departing from the spirit and scope of the present invention. In addition, it should be understood that aspects of the various embodiments may be interchanged both in whole or in part. Furthermore, those of ordinary skill in the art will appreciate that the foregoing description is by way of example only, and is not intended to limit the invention so further described in such appended claims. 

What is claimed is:
 1. A thermotropic liquid crystalline polymer composition that comprises a liquid crystalline polymer melt polymerized in the presence of an aromatic amide oligomer, wherein the polymer composition exhibits a certain complex viscosity determined by a parallel plate rheometer at an angular frequency of 0.15 radians per second, temperature of 350° C., and constant strain amplitude of 1%, and a certain melt viscosity determined by a capillary rheometer at a shear rate of 1000 seconds⁻¹ and temperature of 350° C., wherein the ratio of the complex viscosity to the melt viscosity is from about 50 to about
 1000. 2. The polymer composition of claim 1, wherein the liquid crystalline polymer is wholly aromatic.
 3. The polymer composition of claim 1, wherein the ratio of the complex viscosity to the melt viscosity is from about 150 to about
 500. 4. The polymer composition of claim 1, wherein the complex viscosity is about 3,500 Pa-s or more.
 5. The polymer composition of claim 1, wherein the complex viscosity is from about 10,000 to about 50,000 Pa-s.
 6. The polymer composition of claim 1, wherein the melt viscosity is about 200 Pa-s or less.
 7. The polymer composition of claim 1, wherein the composition has a melting temperature of from about 250° C. to about 400° C.
 8. The polymer composition of claim 1, wherein the liquid crystalline polymer is a wholly aromatic polyester containing repeating units derived from 4-hydroxybenzoic acid and terephthalic acid.
 9. The polymer composition of claim 8, wherein the liquid crystalline polymer also contains repeating units derived from isophthalic acid, hydroquinone, 4,4-biphenol, 2,6-hydroxynaphthoic acid, acetominophen, or a combination thereof.
 10. The polymer composition of claim 1, wherein the aromatic amide oligomer has the following general formula (I):

wherein, rings A and B are independently a 6-membered aromatic ring wherein 1 to 3 ring carbon atoms are optionally replaced by nitrogen or oxygen, wherein each nitrogen is optionally oxidized, and wherein rings A and B may be optionally fused or linked to a 5- or 6-membered aryl, heteroaryl, cycloalkyl, or heterocyclyl; R₅ is halo, haloalkyl, alkyl, alkenyl, aryl, heteroaryl, cycloalkyl, or heterocyclyl; m is from 0 to 4; X₁ and X₂ are independently C(O)HN or NHC(O); and R₁ and R₂ are independently selected from aryl, heteroaryl, cycloalkyl, and heterocyclyl.
 11. The polymer composition of claim 10, wherein rings A and B are phenyl.
 12. The polymer composition of claim 10, wherein m is
 0. 13. The polymer composition of claim 1, wherein the aromatic amide oligomer has the following general formula (IV):

wherein, X₁, X₂, X₄, and X₅ are independently C(O)HN or NHC(O); R₅, R₇, R₈, R₁₀, and R₁₁ are independently selected from aryl, heteroaryl, cycloalkyl, and heterocyclyl; m is from 0 to 4; and p, q, s, and t are independently from 0 to
 5. 14. The polymer composition of claim 13, wherein m, p, and q are 0, and s and t are independently from 0 to
 5. 15. The polymer composition of claim 1, wherein the aromatic amide oligomer has the following general formula (V):

wherein, X₁, X₂, X₃ X₄, X₅, and X₆ are independently C(O)HN or NHC(O); R₅, R₇, R₈, R₉, R₁₀, R₁₁, and R₁₄ are independently selected from halo, haloalkyl, alkyl, alkenyl, aryl, heteroaryl, cycloalkyl, and heterocyclyl; m is from 0 to 3; and p, q, r, s, t, and v are independently from 0 to
 5. 16. The polymer composition of claim 1, wherein the oligomer is selected from the group consisting of the following compounds and combinations thereof: Structure Name

N1,N4-bis(4-benzamidophenyl) terephthalamide

N1,N3,N5-tris(4-benzamidophenyl) benzene-1,3,5-tricarboxamide

N4-phenyl-N1-[4-[[4- (phenylcarbamoyl)benzoyl]amino] phenyl]terephthalamide

N4-phenyl-N1-[3-[[4- (phenylcarbamoyl)benzoyl]amino] phenyl]terephthalamide

N1,N3-bis(4-benzamidophenyl) benzene-1,3-dicarboxamide

N3,phenyl-N1-[3-[[3- (phenylcarbamoyl)benzoyl]amino] phenyl]benzene-1,3-dicarboxamide

N1,N3-bis(3-benzamidophenyl) benzene-1,3-dicarboxamide

N1,N3-bis(4-phenylphenyl)benzene- 1,3-dicarboxamide

N1,N3,N5-tris(3-benzamidophenyl) benzene-1,3,5-tricarboxamide


17. The polymer composition of claim 1, wherein the oligomer is N1,N4-bis(4-benzamidophenyl)terephthalamide or N1,N3,N5-tris(4-benzamidophenyl)-benzene-1,3,5-tricarboxamide.
 18. The polymer composition of claim 1, wherein the oligomer contains from 3 to 12 amide functional groups per molecule.
 19. The polymer composition of claim 1, wherein the oligomer has a molecular weight of from about 450 to about 5,000 grams per mole.
 20. The polymer composition of claim 1, wherein the polymer composition has a melting point of from about 300° C. to about 400° C. 